Glycine–nitrate combustion synthesis of Cu-based nanoparticles for NP9EO degradation applications

Copper-based nanoparticles were synthesized using the glycine–nitrate process (GNP) by using copper nitrate trihydrate [Cu(NO₃)₂·3H₂O] as the main starting material, and glycine [C₂H₅NO₂] as the complexing and incendiary agent. The as-prepared powders were characterized through X-ray diffraction (XRD), Brunauer–Emmett–Teller (BET), X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy analysis. Using Cu(NO₃)₂·3H₂O as the oxidizer (N) and glycine as fuel (G), we obtained CuO, mixed-valence copper oxides (CuO + Cu₂O, G/N = 0.3–0.5), and metallic Cu (G/N = 0.7). The XRD and BET results indicated that increasing the glycine concentration (G/N = 0.7) and reducing the particle surface area increased the yield of metallic Cu. The effects of varying reaction parameters, such as catalyst activity, catalyst dosage, and H₂O₂ concentration on nonylphenol-9-polyethoxylate (NP9EO) degradation, were assessed. With a copper-based catalyst in a heterogeneous system, the NP9EO and total organic carbon removal efficiencies were 83.1% and 70.6%, respectively, under optimum operating conditions (pH, 6.0; catalyst dosage, 0.3 g/L; H₂O₂ concentration, 0.05 mM). The results suggest that the removal efficiency increased with an increase in H₂O₂ concentration but decreased when the H₂O₂ concentration exceeded 0.05 mM. Furthermore, the trend of photocatalytic activity was as follows: G/N = 0.5 > G/N = 0.7 > G/N = 0.3. The G/N = 0.5 catalysts showed the highest photocatalytic activity and resulted in 94.6% NP9EO degradation in 600 min.