Characteristics of polyimide/barium titanate composite films

In this study, the characteristics of the polyimide/BaTiO₃ composite films with various amounts of BaTiO₃ were evaluated. Modifier 1-methoxy-2-propyl acetate was added during composite preparation to disperse the BaTiO₃ particles in polyimide matrix. Conversion of polyamic acid (PAA) to polyimide was not completed for the composite film with a high BaTiO₃ loading (90 wt%). Dielectric constant of the film increases from 3.53 to 46.50, at the sweep frequency of 10 kHz, as the BaTiO₃ content increases from 0 to 90 wt% (0-67.5 vol.%), which is mainly due to the relatively high dielectric constant of BaTiO₃ particles in the polyimide matrix. The dielectric losses at 10 kHz is ranging from 0.005 to 0.015, which is due to the switching of the domain wall. Water absorption decreases considerably with increasing BaTiO₃ content. With 10 wt% (2.5 vol.%) BaTiO₃ addition, the water absorption of the composite film reduces 45% from that of pure polyimide. Also, high loading of BaTiO₃ is not beneficial to reduce the water absorption of the composite film.